Effects of internal stress on remanence intensity jumps across the Verwey transition for multi-domain magnetite

Qingsong Liu*, Yongjae Yu, Adrian R. Muxworthy, Andrew P. Roberts

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

9 Citations (Scopus)

Abstract

The magnetic properties of magnetite (Fe3O4) are strongly dependent on the internal stress related to stress-controlled regions and to closure domains associated with defects. The contribution of internal stress to the low-temperature magnetic properties of magnetite was tested using annealed and unannealed multi-domain (MD) magnetites. During low-temperature cooling, a room temperature-induced saturation isothermal remanent magnetization (SIRM) increased abruptly at the Verwey transition (Tv ∼ 122 K). In particular, the absolute intensity jump (δVJ, defined as the jump in SIRM at Tv upon cooling) resulted from the high-coercivity fraction of MD grains. We observe that annealing significantly reduces internal stress and thus decreases the average microcoercivity. Comparison of the alternating field (AF) demagnetization spectra of δVJ both for annealed and unannealed magnetites directly links δVJ to the internal stress. It is likely that removal of the closure domain associated with stress-controlled regions was dominant when the peak AF was less than the average micromagnetic coercivity 〈hc〉, resulting in a net increase of δVJ with increasing AF. However, when the AF exceeded the 〈hc〉 threshold, δVJ decreased because the stress-controlled regions were demagnetized. Such observations could therefore be useful for estimating the 〈hc〉 of MD magnetite.

Original languageEnglish
Pages (from-to)100-107
Number of pages8
JournalPhysics of the Earth and Planetary Interiors
Volume169
Issue number1-4
DOIs
Publication statusPublished - Aug 2008
Externally publishedYes

Fingerprint

Dive into the research topics of 'Effects of internal stress on remanence intensity jumps across the Verwey transition for multi-domain magnetite'. Together they form a unique fingerprint.

Cite this