Ge11.5As24Se64.5 chalcogenide glass nanowires with a nonlinear parameter of 136,000W-1km-1 at 1550nm

Xin Gai*, Duk Yong Choi, Steve Madden, Douglas Bulla, Barry Luther-Davies

*Corresponding author for this work

    Research output: Chapter in Book/Report/Conference proceedingConference contributionpeer-review

    Abstract

    We have fabricated nanowires from Ge11.5As24Se 64.5 glass. The loss of nanowire was measured to be 2.6dB/cm for fundamental TM mode. The nonlinear coefficient (γ) was determined to be ≈136±7W-1m-1 at 1550nm. Supercontinuum (SC) was produced in an 18mm long nanowire.

    Original languageEnglish
    Title of host publication2010 Conference on Optoelectronic and Microelectronic Materials and Devices, COMMAD 2010 Proceedings
    Pages231-232
    Number of pages2
    DOIs
    Publication statusPublished - 2010
    Event2010 Conference on Optoelectronic and Microelectronic Materials and Devices, COMMAD 2010 - Canberra, ACT, Australia
    Duration: 12 Dec 201015 Dec 2010

    Publication series

    NameConference on Optoelectronic and Microelectronic Materials and Devices, Proceedings, COMMAD

    Conference

    Conference2010 Conference on Optoelectronic and Microelectronic Materials and Devices, COMMAD 2010
    Country/TerritoryAustralia
    CityCanberra, ACT
    Period12/12/1015/12/10

    Fingerprint

    Dive into the research topics of 'Ge11.5As24Se64.5 chalcogenide glass nanowires with a nonlinear parameter of 136,000W-1km-1 at 1550nm'. Together they form a unique fingerprint.

    Cite this