Nanoindentation-induced deformation of Ge

The deformation mechanisms of crystalline (100) Ge were studied using nanoindentation, cross sectional transmission electron microscopy (XTEM) and Raman microspectroscopy. For a wide range of indentation conditions using both spherical and pointed indenters, multiple discontinuities were found in the force-displacement curves on loading, but no discontinuities were found on unloading. Raman microspectroscopy, measured from samples which had plastically deformed on loading, showed a spectrum shift from that in pristine Ge, suggesting only residual strain. No evidence (such as extra Raman bands) was found to suggest that any pressure-induced phase transformations had occurred, despite the fact that the material had undergone severe plastic deformation. Selected area diffraction pattern studies of the mechanically damaged regions also confirmed the absence of additional phases. Moreover, XTEM showed that, at low loads, plastic deformation occurs by twinning and dislocation motion. This indicates that the hardness of Ge measured by indentation is not primarily dominated by phase transformation, rather by the nucleation and propagation of twin bands and/or dislocations.