Synergizing Phase and Cavity in CoMoO_xS_y Yolk–Shell Anodes to Co-Enhance Capacity and Rate Capability in Sodium Storage

Sodium-ion batteries (SIBs) have been recognized as the promising alternatives to lithium-ion batteries for large-scale applications owing to their abundant sodium resource. Currently, one significant challenge for SIBs is to explore feasible anodes with high specific capacity and reversible pulverization-free Na⁺ insertion/extraction. Herein, a facile co-engineering on polymorph phases and cavity structures is developed based on CoMo-glycerate by scalable solvothermal sulfidation. The optimized strategy enables the construction of CoMoO_xS_y with synergized partially sulfidized amorphous phase and yolk–shell confined cavity. When developed as anodes for SIBs, such CoMoO_xS_y electrodes deliver a high reversible capacity of 479.4 mA h g⁻¹ at 200 mA g⁻¹ after 100 cycles and a high rate capacity of 435.2 mA h g⁻¹ even at 2000 mA g⁻¹, demonstrating superior capacity and rate capability. These are attributed to the unique dual merits of the anodes, that is, the elastic bountiful reaction pathways favored by the sulfidation-induced amorphous phase and the sodiation/desodiation accommodatable space benefits from the yolk–shell cavity. Such yolk–shell nano-battery materials are merited with co-tunable phases and structures, facile scalable fabrication, and excellent capacity and rate capability in sodium storage. This provides an opportunity to develop advanced practical electrochemical sodium storage in the future.